  • High Consistency Rubber for Calendering (with Fumed Silica)

High Consistency Rubber for Calendering (with Fumed Silica)

This product has been discontinued and removed from our shelves.

High Consistency Rubber for Calendering (with Fumed Silica)
Inquiry
Applications

This high consistency rubber is suited to be used in calendering process for manufacturing various types of silicone rubber sheet products.

  • Applications
Features
  • Fast calendering;
  • High size consistency;
  • Non-yellowing;
  • Outstanding aging resistance;
  • Excellent processability;
Approvals

ROHS, REACH, FDA, FLGB, CA65, EN71-3, EN14372, PAHS, PFOA, CPSIA, siloxane testing, etc.

Test

Addition A type agent 0.5%, B type agent 0.8%, 120℃×3min×15Mpa

Technical Data
  • Model: HT-9932P
  • Appearance: Translucent
  • Processability: 200-200
  • Hardness (Shore A): 30
  • Density (g/cm3): 1.12
  • Tensile strength (Mpa): 7
  • Elongation (%): 850
  • Tear strength (K N/m): 15
  • Model: HT-9942P
  • Appearance: Translucent
  • Processability: 220-240
  • Hardness (Shore A): 40
  • Density (g/cm3): 1.13
  • Tensile strength (Mpa): 7
  • Elongation (%): 750
  • Tear strength (K N/m): 15
  • Model: HT-9952P
  • Appearance: Translucent
  • Processability: 220-240
  • Hardness (Shore A): 50
  • Density (g/cm3): 1.14
  • Tensile strength (Mpa): 7
  • Elongation (%): 650
  • Tear strength (K N/m): 15
  • Model: HT-9962P
  • Appearance: Translucent
  • Processability: 230-260
  • Hardness (Shore A): 60
  • Density (g/cm3): 1.15
  • Tensile strength (Mpa): 7
  • Elongation (%): 550
  • Tear strength (K N/m): 15
  • Model: HT-9972P
  • Appearance: Translucent
  • Processability: 260-280
  • Hardness (Shore A): 70
  • Density (g/cm3): 1.2
  • Tensile strength (Mpa): 7
  • Elongation (%): 450
  • Tear strength (K N/m): 15
  • Model: HT-9982P
  • Appearance: Translucent
  • Processability: 250-280
  • Hardness (Shore A): 80
  • Density (g/cm3): 1.2
  • Tensile strength (Mpa): 7
  • Elongation (%): 300
  • Tear strength (K N/m): 15